Wednesday, July 19, 2006
The owner of this board wanted to get back into surfing. He is the second owner. A mate of his purchased it while on a trip to the US. It was in pretty poor condition.
The stringer is 2" balsa or I should say was balsa. It was completely rotted and had to be replaced. It has a timber fin with inlays. This was also restored.
The board was sanded to expose all the dings and old repairs. The remains of the balsa stringer were removed. This meant cutting down each side of the stringer with a diamond saw and scraping the rotted timber out. The foam is in excellent condition. Probably protected by the glue used to glue up the stringer.
The original timber fin has been rebuilt and reset. All the old glass was removed. The timber was carefully sanded to remove all the excess glass and resin and to expose the inlay work. The trailing edge had to be replaced. Western Red Cedar was used. Two sealing coats of resin were applied. Then two layers of 10oz laminated to one side with 10mm of cloth overhanging. This side was then filler coated. The overhang was used to mould the continuous rovings, used to form the clear bead around the fin. Once cured the bead was sanded and two layers of 10oz were applied to the fin. Filler coated and sanded ready for setting onto the board. Once the fin was set, the board was filler coated and sanded ready for the pigment work.
The stringer and rails were masked and the pigment coats brushed on. I use a mixture of surfboard lam resin and neutral spray gelcoat. 75% resin 25% gelcoat and 3% Wax in Styrene. The gelcoat is designed to cling to vertical surfaces. This helps on the rails to minimise sagging and separation. The gelcoat ups the geltime slightly without having to use higher catalyst percentages. The board was sanded ready for glossing.
Friday, July 14, 2006
This board was found at a local NSW Central Coast market, in 2002, cost $200. The board was in poor condition and covered with non-original white gelcoat. Possible tail section missing. The original fin was missing and had been replaced with a 1970's Bahne-type fin-box (Multifins?) and plastic fin. See pre and post restoration photographs below. The condition of this board prior to restoration; on a scale of 1-10 would have been 2-21/2. The board was white all over. Probably not original because it covered the manufactures logo and the foam was quiet brown. It had major dings on the tail and nose, stress marks on the bottom, and fractures and dings all around the rails. The board was in such poor condition, there was no choice but to do a full pigment job. All the pigment / gelcoat was sanded off revealing the "King " logo and the wedge stringer on the deck. The fin box had to be removed and the step area rebuilt. The rails had to be faired and glassed, stress marks and dings repaired, and a new fin made and glassed in. Pigment coats applied, pin lined, wet & dry sanded and polished. A total of 40 hours work over a six month period.
No clear photo could be found, of a fin template for an Australian version of this type of board. The only photo shows the board on its side. The fin looks as if it could be a reverse d fin. So that is what we went with. The dimentions are. Base 10.5 inches and Height 9 inches.
Thursday, July 13, 2006
This board was purchased from a work colleague for AU $100. The deck was in good condition, apart from the manufactures logo delaminating, and some large dents in the nose. These dents I think are due to the lack of glass on the nose on the bottom. The bottom was another story. No glass, for the fist two and half feet. from the nose. This resulting in the stringer being completely rotted for the whole length of the board. The stringer may have been Pacific Maple or Western red ceder. The rails had the usual amount of dings and fractures for a board of this age. The fin was intact and in good condition.
The first task was to replace the glass missing from the nose with two layers of 10 oz cloth. Next, replace the stringer, This meant cutting the glass on either side of the stringer with a diamond saw and scraping out the sludge with a chisel. The fin was not removed from the board. The original stringer was 20min wide which ment 25mm DAR fitted straight in. I laminated five lengths of 20min by 20min Pacific maple, using FGI RI 80 epoxy resin and AEROSIL silica, and clamped in place. After planing the excess timber off the stringer, 150min either side of the stringer was heavily ground and two layers of 10 oz cloth applied after sealing the stringer with a coat of resin. All the other dings where ground, reglassed and sanded. The whole board was then sanded and all the low spots filled and faired with 75% Q-CELL / 25% AEROSIL. Once fair all the filled areas were covered with one layer of 4oz cloth.
After sanding it was time for the pigment coats to hide the ugly spots. The deck was left clear as original. The rails were pigmented a dark green to the trim lines on the top and bottom. The bottom was pigmented a peppermint green leaving the stringer clear. The rails needed two coats, which has now become standard practice on all the restorations I've done since. After sanding to 1200 w&d a 1/4- black pinline was added top and bottom on the trim line. The board was then sanded with 1500 w&d and polished. The resin on the deck is original and did not need any extra work done to bring the gloss up.